Abstract:
To remove residual stresses, an as-built SLM object is usually post-treated. This treatment can affect the microstructure, changing the final mechanical characteristics. This investigation is focused on the microstructural characterisation of 316L austenitic stainless steel in as-built and annealed conditions. The SLM microstructure was relatively stable up to 900°C, when cell boundaries start to disappear. At higher temperatures, an insignificant grain coarsening was detected. These microstructural changes caused a gradual drop in the hardness. The obtained result is background for the future development of post-treatment regimens to achieve a high level in the final mechanical properties of SLM objects.