Abstract:
Mechanical properties, porosity, and microstructure of Ti6Al4V (ELI) material produced by Selective Laser Melting (SLM) under controlled oxygen content were analyzed. Fully martensitic α’structure with high dislocation density and stacking faults was observed in both as-built and stress relieved samples by means of XRD and TEM. Tensile {101 ̅2} twinning was identified by TEM and electron diffraction. Accommodation of thermal stresses during manufacturing was suggested as a possible reason for twinning. Computed tomography of pores was carried out. Pores in the specimens were evenly distributed and mostly had an elongated shape. Defect analysis by micro CT scans in pre-strained samples confirmed that the pore coalescence was the main crack formation mechanism in the final fracture with typical cup-and-cone fracture morphology. Additionally, typical dimples and quasi-cleavage were revealed. Mechanical properties of the samples after stress relieving heat treatment at 650°C for 3 h are complied with the international standard for Ti alloys for biomedical applications.